Morphology of the particles of by-products of steel rolling production


Views: 95 / PDF downloads: 56

Authors

  • Д Каргин
  • А Козловский
  • Е Алтынов
  • Ж Касымханов
  • А Бисекен
  • Д Мухамбетов

DOI:

https://doi.org/10.32523/2616-6836-2019-129-4-59-64

Abstract

This paper presents the results of the study of the morphological properties of the by-products of steel rolling
production - mill scale and oxide powder obtained by spray pyrolysis of spent pickling solution. Non-alloyed low-carbon steel containing the minimum amount of impurities was used as the initial object of study. The study of the structural characteristics and elemental composition of by-products was carried out using a Hitachi TM3030 scanning electron microscope with a Bruker XFlash MIN SVE microanalysis system with an accelerating voltage of 15 kV. It has been established that mill scale consists of small particles ranging in size from fractions of a micron to ∼ 100 microns, which are conglomerates of porous spherical
structures with a diameter in the range from about 100 to 300 nm. Powdered hematite obtained from spent pickling solution is a hollow microparticle of spherical shape, the average size of which is 120-140 microns.

Downloads

Published

2022-07-05

How to Cite

Каргин, Д., Козловский, А., Алтынов, Е., Касымханов, Ж., Бисекен, А., & Мухамбетов, Д. (2022). Morphology of the particles of by-products of steel rolling production. BULLETIN OF THE L.N. GUMILYOV EURASIAN NATIONAL UNIVERSITY. PHYSICS. ASTRONOMY SERIES, 129(4), 59–64. https://doi.org/10.32523/2616-6836-2019-129-4-59-64

Issue

Vol. 129 No. 4 (2019)

Section

Статьи

Most read articles by the same author(s)